What is the difference between A2 and A4 stainless?

A2 grade corresponds to SS 304 (18% chromium, 8% nickel) - good for general and indoor use. A4 grade is SS 316 (16% chromium, 10% nickel, 2% molybdenum) - molybdenum dramatically improves pitting resistance in chloride-containing environments like seawater. A4 costs 25-40% more but lasts decades longer in marine service.

What does 70 / 80 mean in A2-70 / A4-80?

The number is the minimum tensile strength in 10 MPa units. A2-70 stainless reaches 700 MPa minimum tensile strength. A4-80 reaches 800 MPa. The cold-working that produces these strengths makes the steel slightly magnetic - this is normal for cold-worked austenitic stainless.

Is stainless steel really non-magnetic?

Austenitic stainless (304, 316) is non-magnetic in fully annealed condition. Cold working - which happens during fastener forming - disrupts the austenite structure and introduces slight ferromagnetism. This is normal and does not indicate the wrong grade or quality issue.

When should I use 316L instead of 316?

The L stands for low carbon (max 0.03% C vs 0.08% in standard 316). Use 316L whenever the fastener will be welded - the low carbon prevents chromium carbide precipitation at grain boundaries during welding, which would otherwise cause inter-granular corrosion in service.

Do you passivate stainless fasteners?

Yes. All finished stainless fasteners go through nitric acid or citric acid passivation per ASTM A967. The process removes free iron from the surface and restores the chromium oxide passive layer that gives stainless its corrosion resistance.

Can stainless fasteners gall during installation?

Yes - austenitic stainless (304 and 316) is prone to thread galling when stainless mates with stainless under load. We recommend using anti-seize lubricant on threads, installing at slower torque rates, and pairing different grades when possible (e.g., 316 bolt with 304 nut).

<span class ="tr_" id="tr_0" data-source="" data-srclang="en" data-orig="Premier Stainless Steel Fasteners Factory in China | 304, 316, 316L — Kbear Metal">Premier Stainless Steel Fasteners Factory in China | 304, 316, 316L — Kbear Metal</span>

Vodilni KITAJSKI IZ NERJAVEČEGA JEKLA · OD LETA 1989

Premier pritrdilni elementi iz nerjavečega jekla: Odporen proti koroziji od tuljave do kartona

Kbear Metal proizvaja pritrdilne elemente A2-70 (SS 304), A4-80 (SS 316) in SS 316L v sornikih, maticah, vijakih in podložkah. Pasivirana končna obdelava, preverjena s solnim razpršilom, certificirana za pomorske, prehrambene, kemične in arhitekturne storitve.

Zahtevaj ponudbo SS → Oglejte si izdelke SS

304/316/316L

Izdelane ocene

A2/A4

Razredi lastnosti

M2–M48

Razpon velikosti

// Specifikacije proizvodnje nerjavnega jekla

OceneSS 304 · 316 · 316L · 410

Razred lastnostiA2-50/70 A4-50/70/80

StandardiDIN · ISO · ASTM · JIS

PovršinaPasivirano · Polirano · BSO

MOQ50 kg / SKU

Čas izvedbe15–25 dni

35 let

Od leta 198935+ let v proizvodnji

ISO

ISO 9001 / IATFCertificiran sistem kakovosti

40+

40+ izvoznih trgovZDA · EU · MENA · APAC

24h

24-urni odgovorPonudba v enem delovnem dnevu

// Linije izdelkov Bolt

Nerjaveči pritrdilni elementi v vseh kategorijah

Celoten nabor nerjavnih pritrdilnih elementov, proizvedenih na namenskih linijah samo za nerjavno jeklo.

// 01

SS šestrobi vijaki

Šestrobi vijaki iz nerjavečega jekla 304, 316 in 316L. Razredi A2-70 in A4-80 za pomorske in kemične storitve.

OD 933OD 931A2/A4

// 02

SS šestrobe matice

Standardne šestrobe matice, protimatice in matice s prirobnico v ustreznih razredih iz nerjavečega jekla.

OD 934OD 985A4-80

// 03

SS vijaki z vtičnico

Notranji inbus vijaki z vtičnico iz nerjavečega jekla 304 in 316. Poliran ali pasiviran zaključek.

OD 912ISO 4762

// 04

SS strojni vijaki

Ploščati, ploski, ovalni in okrogli strojni vijaki v Phillips, Pozi, Torx, pogonih z režami.

OD 84OD 7985OD 965

// 05

SS samorezni vijaki

Samorezni in samovrtalni vijaki iz nerjavečega jekla 304 za zunanjo uporabo v pločevini.

OD 7981DIN 7504

// 06

SS podložke

Ploščate podložke, vzmetne podložke, podložke za blatnike in zobate zaklepe iz nerjavečega jekla 304 in 316.

OD 125OD 127DIN 9021

// 07

SS vijaki

B8, B8M (ASTM A193) dvostranski navojni čepi za kemične in petrokemične storitve prirobnic.

ASTM A193B8 / B8M

// 08

SS očesni vijaki

Kovani dvižni očesni vijaki in obročni vijaki iz nerjavečega jekla SS 316 za uporabo v pomorstvu, vrvju in na morju.

OD 580A4

// 09

Pomorska strojna oprema

Posebni ladijski SS pritrdilni elementi — preklopni vijaki, pritrdilne ušesca, U-sorniki in cevne objemke.

316LNavada

// Tehnične specifikacije

Vrsta in lastnost nerjavečega jekla

Standardne vrste nerjavečega jekla, proizvedene v naši tovarni, in njihove tipične uporabe.

Ocena	Razred lastnosti	LES	Magnetna?	Najboljša aplikacija
SS 304 (A2)	A2-50 / A2-70	18–19	Rahlo (hladno obdelano)	Splošno, hrana, notranji
SS 316 (A4)	A4-50 / A4-70 / A4-80	24–26	Rahlo	Morski, kemični, obalni
SS 316L	A4 (nizkoogljična)	24–26	Rahlo	Varjeni ladijski sklopi
SS 410	C1/C3	11–12	Da (martenzitno)	Samorezni strešni vijaki
SS 17-4PH	Navada	17	Rahlo	Letalstvo, nafta & plin
SS 254 WE	A8	42+	Rahlo	Super korozivna morska voda
SS Duplex 2205	Navada	34–38	ja	Visoka trdnost na morju

// Izbira materiala

Nerjavni razredi za vsako korozijsko okolje

Ujemajte razred z zahtevami po izpostavljenosti kloridom, temperaturi in obremenitvi.

// Avstenitni

304/304L/321

Splošna odpornost proti koroziji

// Marine

316 / 316L / 316Ti

Storitev slane vode in klorida

// Martenzitno

410/416/420

Trdota, samovrtalne konice

// Feritno

430 / 434

Blaga korozija, nizki stroški

// Duplex

2205 / 2507

Visoka trdnost + korozija

// Super avstenitno

254 SMO · 904L

Huda kloridna storitev

// Padavine

17-4PH · 17-7PH

Aerospace, visoka trdnost

// Posebnost

Zlitina 20 · Hastelloy

Huda kemična storitev

// Postopek izdelave vijakov

Kako nerjaveče pritrdilo postane dokončan del

Proizvodne linije samo iz nerjavečega jekla preprečujejo kontaminacijo z ogljikovim jeklom.

SS žica / palica

Nerjavna žica, pregledana s spektrometrom za preverjanje stopnje.

Hladna smer

Namenske stiskalnice iz nerjavečega jekla preprečujejo navzkrižno kontaminacijo.

Navijanje navojev

Trdo kromirane valjarske matrice imajo lastnosti utrjevanja nerjavnega jekla.

Raztopina žarjenja

Po potrebi so deli žarjeni v raztopini za obnovitev avstenitne strukture.

Pasivacija

Pasivacija z dušikovo ali citronsko kislino odstrani prosto železo in obnovi film kromovega oksida.

QC & Pack

Magnetno testiranje, preverjanje stopnje PMI, pakiranje.

// Zagotavljanje kakovosti

Real 316L — potrjen s spektrometrom.

Največje tveganje pri nabavi nerjavečih pritrdilnih elementov je zamenjava stopnje — 201, ki se prodaja kot 304, ali 304, ki se prodaja kot 316. Naše testiranje PMI na vhodnem materialu in končnih serijah odkrije goljufije glede stopnje pred pošiljanjem delov.

ISO

ISO 9001:2015Vodenje kakovosti

IATF

IATF 16949Pripravljen za avtomobile

CE / CPRGradbeništvo EU

SGS

SGS / BVTestiranje tretjih oseb

Testiranje stopnje PMI

Pozitivna identifikacija materiala (PMI) preko rentgenske fluorescence preveri vsebnost kroma, niklja in molibdena.

Test pasivnosti

Test bakrovega sulfata ali feroksila potrjuje, da je bilo prosto železo odstranjeno po kislinski pasivaciji.

Preskus odpornosti proti luknjicam

Preskus železovega klorida ASTM G48 preverja odpornost proti luknjicam za visokokakovostne pomorske pritrdilne elemente.

Mehansko testiranje

Natezna trdnost, preverjena glede na najmanjši razred lastnosti A2-70 / A4-80 po ISO 3506.

// Kam pošiljajo naši vijaki

Industrije, ki potrebujejo nerjavne pritrdilne elemente

Kjer koli korozija napade ogljikovo jeklo, nerjavni pritrdilni elementi zaslužijo svojo ceno.

Marine & Čoln

Nerjaveče jeklo 316L za odpornost proti koroziji v slani vodi.

// A4-80

Predelava hrane

304 iz nerjavečega jekla izpolnjuje kontaktne zahteve FDA za živilsko opremo.

//A2-70

Farmacevtski

Nerjaveče jeklo 316L za sestave opreme za čiste prostore in sterilno opremo.

// A4-80 SS 316L

Arhitekturni

Polirani 304 in 316 za fasade, ograje in dekorativne obloge.

//A2/A4

Kemične tovarne

316L, Duplex 2205 in 254 SMO za težke kemične storitve.

// A4 / A8

Nafta na morju & Plin

316L, Duplex in Super Duplex pritrdilni elementi za strukture ploščadi.

// A4-80 / Duplex

Solarna montaža

304 iz nerjavečega jekla za zunanje fotovoltaične montažne strukture.

//A2-70

Bazen & Vodni

Nerjaveče jeklo 316L je odporno na bazenski klor in bazene s slano vodo.

// A4-80

Želite preizkusiti kakovost nerjavnega jekla pred množičnim naročilom? Brezplačni vzorci 304/316 — preverite z lastnim testerjem PMI.

Zahtevaj SS vzorce →

// Prednosti kupca

Zakaj distributerji izberejo Kbear za nerjavno jeklo

Šest neposrednih tovarniških prednosti pri naročilih nerjavnih pritrdilnih elementov.

// 01

Namenske SS linije

Proizvodnja nerjavečega jekla poteka na ločenih stiskalnicah za glavo in navoje — brez navzkrižne kontaminacije z ogljikovim jeklom.

// 02

Standard testiranja PMI

Vsaka serija je bila preverjena z rentgensko fluorescenco za potrditev stopnje — brez presenečenj 201 namesto 304.

// 03

Interna pasivizacija

Linije za pasiviranje dušikove in citronske kisline odstranijo prosto železo pred odpremo.

// 04

316L za varjenje

316L z nizko vsebnostjo ogljika, posebej založen za varjene sestave v pomorstvu in kemičnih obratih.

// 05

Polirani zaključki

Zrcalno polirani in brušeni zaključki so na voljo za arhitekturne in dekorativne namene.

// 06

Dokumentacija

Certifikati za mlin EN 10204 3.1 in poročila o mehanskih preskusih ISO 3506 z vsako pošiljko.

// Znotraj tovarne

Znotraj našega proizvodnega območja samo iz nerjavečega jekla

Namenske stiskalnice iz nerjavečega jekla, trdo kromirane matrice za valjanje navojev, posode za pasiviranje in postaje za testiranje PMI.

Workshop overview — Kbear Metal fastener factory

// 01 · Delavnica

28.000 m² proizvodnega prostora

// 02 · Hladna smer

Stiskalnice z več postajami

// 03 · Navijanje navojev

12 navojnih vrvic

// 04 · Toplotna obdelava

Kontinuirane peči z mrežastim trakom

// 05 · QC Lab

In-line pregled

// 06 · Pakiranje & Nalaganje

Pošiljanje, pripravljeno za izvoz

// Watch Production

Oglejte si izdelavo nerjavnih pritrdilnih elementov

Trije kratki videoposnetki, ki prikazujejo nerjavno žico, pasivacijo in preverjanje stopnje PMI – stvari, ki ujamejo goljufije pri oceni.

02:14

// 01 · Proizvodnja

Hladna glava do valjanja navojev

Hladno obdelana nerjavna jeklena palica na namenskih stiskalnicah samo za nerjaveče — brez navzkrižne kontaminacije z ogljikovim jeklom.

01:48

// 02 · Kontrola kakovosti

Inšpekcija & Postopek testiranja

Preverjanje stopnje rentgenske fluorescence PMI, testiranje pasivacije in preverjanje nateznosti po ISO 3506.

01:32

// 03 · Pakiranje & Pošiljanje

Pakiranje v nakladanje kontejnerja

Pasivirani, polirani nerjavni pritrdilni elementi, pakirani in poslani kupcem v pomorstvu, hrani in kemikalijah.

Brezplačni vzorci

Standardni vzorci pritrdilnih elementov so brezplačno poslani v oceno. Krijete samo stroške hitre dostave.

Inšpekcija prvega reda

Pregled tretje osebe SGS ali BV pri vašem prvem naročilu na naše stroške – preverite pred plačilom stanja.

Samo 30 % depozit

T/T 30-odstotni depozit spravi vaše naročilo v proizvodnjo. 70 % stanja po pregledu pred odpremo.

Kakovostna zamenjava

Vsako napako zunaj dogovorjenega AQL bomo brezplačno zamenjali pri naslednji pošiljki, brez vprašanj.

// Vprašanja kupcev vijakov

Pogosta vprašanja o pritrdilnih elementih iz nerjavečega jekla

Hitri odgovori o izbiri razreda, pasivizaciji in korozijski učinkovitosti.

Kakšna je razlika med A2 in A4 nerjavnim jeklom?

Razred A2 ustreza SS 304 (18 % kroma, 8 % niklja) — primeren za splošno in notranjo uporabo. Razred A4 je SS 316 (16 % kroma, 10 % niklja, 2 % molibdena) – molibden dramatično izboljša odpornost proti luknjicam v okoljih, ki vsebujejo kloride, kot je morska voda. A4 stane 25–40 % več, vendar zdrži desetletja dlje v pomorski uporabi.

Kaj pomeni 70 / 80 v A2-70 / A4-80?

Število je najmanjša natezna trdnost v enotah 10 MPa. Nerjavno jeklo A2-70 doseže minimalno natezno trdnost 700 MPa. A4-80 doseže 800 MPa. Hladna obdelava, ki povzroči te trdnosti, naredi jeklo rahlo magnetno – to je normalno za hladno obdelano avstenitno nerjavno jeklo.

Je nerjavno jeklo res nemagnetno?

Avstenitno nerjavno jeklo (304, 316) je v popolnoma žarjenem stanju nemagnetno. Hladna obdelava – ki se zgodi med oblikovanjem pritrdilnih elementov – poruši strukturo avstenita in povzroči rahel feromagnetizem. To je normalno in ne pomeni napačne stopnje ali težave s kakovostjo.

Kdaj naj uporabim 316L namesto 316?

L pomeni nizko vsebnost ogljika (največ 0,03 % C proti 0,08 % v standardu 316). Uporabite 316L, kadar koli boste varili pritrdilni element — nizka vsebnost ogljika preprečuje obarjanje kromovega karbida na mejah zrn med varjenjem, kar bi sicer med delovanjem povzročilo intergranularno korozijo.

Ali pasivirate nerjavne pritrdilne elemente?

ja Vsi končni pritrdilni elementi iz nerjavečega jekla gredo skozi pasivacijo dušikove ali citronske kisline po ASTM A967. Postopek odstrani prosto železo s površine in obnovi pasivno plast kromovega oksida, ki daje nerjavnemu jeklu odpornost proti koroziji.

Ali lahko nerjavni pritrdilni elementi med namestitvijo žolčijo?

Da — avstenitno nerjavno jeklo (304 in 316) je nagnjeno k trganju navojev, ko se nerjavno jeklo pod obremenitvijo spaja z nerjavnim jeklom. Priporočamo, da na navojih uporabite mazivo proti zagozdenju, namestitev s počasnejšimi stopnjami navora in združevanje različnih razredov, kadar je to mogoče (npr. vijak 316 z matico 304).

Stiki

KBEAR CETAL FACTORY

Zanggezude v industrijskem paketu, Create, Kitajska

Sedež

[email protected]

Podpora

+86 18562662895